GNEE STEEL huwa fornitur ta 'l-azzar professjonali. GNEE Global Enterprises stands għoli b'impronta internazzjonali impressjonanti, li jesportaw il-prodotti tiegħu għal aktar minn 70 pajjiż u reġjun. Mill-Istati Uniti sal-Unjoni Ewropea, il-prodotti tagħna kisbu reputazzjoni qawwija għall-kwalità u s-servizzi eċċezzjonali tagħhom. Aħna kburin li waqqafna ruħna bħala attur globali affidabbli fl-industrija tagħna.
Riċerka dwar it-toughness f'temperatura baxxa ta 'pjanċi reżistenti għall-ilbies
Il-pjanċa reżistenti għall-ilbies hija l-aktar azzar komuni użat fil-makkinarju tal-inġinerija. Dan l-azzar jeħtieġ toughness tajba f'temperatura baxxa u weldjabbiltà taħt ebusija għolja. Dan l-artikolu l-ewwel juża l-istudju sperimentali tat-toughness tal-impatt taħt serje ta 'temperaturi, minħabba li huwa relattivament faċli li jitkejjel l-indiċi tal-enerġija materjali u r-riżultati tat-test huma relattivament sinjuri u maturi. Madankollu, l-indiċi tat-toughness tal-impatt għadu diffiċli biex jipprovdi evalwazzjoni effettiva tas-sikurezza. Fid-dawl ta 'dan, dan id-dokument juża test tad-dmugħ dinamiku (DT) qrib id-daqs attwali biex jistudja aktar it-toughness f'temperatura baxxa tal-pjanċa reżistenti għall-ilbies. Ir-riżultati tat-test juru li kemm l-impatt tas-serje kif ukoll id-dmugħ dinamiku juru plateau ta 'fuq ogħla u temperatura ta' transizzjoni fraġli-duttili aktar baxxa. , il-materjal għandu toughness tajba f'temperatura baxxa.
Il-materjal sperimentali huwa JFE-C400 pjanċa reżistenti għall-ilbies. Il-proċess ta 'produzzjoni tiegħu huwa: konvertitur + raffinar LF barra l-forn → ikkastjar tal-moffa → rolling bis-sħana → modulazzjoni (tifi + ittemprar). Il-ħxuna tal-pjanċa hija 4{{10}}mm, u l-kompożizzjoni kimika hija (frazzjoni tal-massa, %) :0.10C, 0.28Si, 0.42Mn, 0.001S,<0.005P, 3.0Ni, 1.0Cr, 0.25Mo. Samples were taken transversely along the surface and center of the wear-resistant plate, and standard specimens were processed according to the provisions of GB/T228-2002 "Metal Materials Room Temperature Tensile Test Method", and conventional tensile and Z-direction tensile tests and a series of impact tests were conducted. According to GB/T5482-2007 "Metal Materials Dynamic Tear Test Method", samples were taken and processed into 180mm×40mm×16mm specimens for a series of dynamic tear tests. The opening direction of the specimens was perpendicular to the rolling direction. The metallographic structure and grain size were corroded by 4% nitric alcohol, saturated picric acid + a small amount of detergent respectively. The tensile fracture morphology was observed using S4300 scanning electron microscope.
Pjanċi reżistenti għall-ilbies prodotti industrijalment għandhom ħbub fini u strutturi uniformi. Il-pjanċi reżistenti għall-ilbies għandhom temperatura ta 'transizzjoni baxxa minn iebsa għal fraġli u toughness tajba f'temperatura baxxa, li tiggarantixxi s-sigurtà tal-makkinarju tal-inġinerija. Fil-metodu ta 'riċerka ta' toughness ta 'temperatura baxxa, jinstab li t-test tad-dmugħ dinamiku fuq skala kbira jista' jiżvela aktar il-karatteristiċi tat-tranżizzjoni duttili-fraġli.